| Product: | RTV-200 | RTV-831 | RTV-835 | RTV-847 | RTV-863 | RTV-228 | |
|---|---|---|---|---|---|---|---|
| Color | Translucent | White | Dark Red | White | White | Reddish brown | |
| Ration | by weight | 100:05 | 100:05 | 100:05 | 100:05 | 100:05 | 100:100 |
| Mix. Visc. | (*CpS)mPa.s | 1,3 mio. | 50.000 | 20.000 | 30.000 | 45.000 | (7500)* |
| Pot life | min. | 90 | 60 | 60 | 60 | 60 | 15-20 |
| Gel time | min. | 45 | 30 | 30 | 30 | 30 | 15 |
| Demould time | Hours | 12-18 | 24 | 24 | 24 | 24 | 2 |
| Type of curing* | Condensation | Condensation | Condensation | Condensation | Condensation | Addition | |
| Density Mixed | g/cm³ | 1,1 | 1,12 | 1,5 | 1,12 | 1,12 | 1,1 |
| Shore A | 23 | 8 | 55 | 17 | 25 | 28 | |
| Linear shrinkage | % | 0,8 | 0,8 | 0,5 | 0,8 | 0,8 | 0,1 |
| Tensile strength | Mpa | 3 | 3 | 3 | 3 | 4,0 | 7,5 |
| Elongation | % | 500 | 600 | 65 | 600 | 500 | 450 |
| Tear strength | N/mm | 18 | 18 | 13 | 17 | 21 | 20 |
| Shrinkage 40°C | % | ||||||
| Shrinkage 60°C | % | ||||||
| Expansion 40°C | % | ||||||
| Temp. Resistans | °C | -50-+120 | -50-+120 | -50-+350 | -50-+120 | -50-+120 | -70-+200 |
| Pack size | 22 kg A + 1,1 kg Cat. | 25 kg A + 1,25 kg Cat | 25 kg A + 1,25 kg Cat | 25 kg A + 1,25 kg Cat | 25 kg A + 1,25 kg Cat | 25 kg A + 25 kg B | |
| Shelf life | 3-6 months | 1 year | 1 year | 1 year | 1 year | 1 year | |
| Remarks/ Application | Thixotropic rubber | Electronic | Metal casting | Allround | High Strength | Tampon |
| Product: | RTV-233 | RTV-250 | RTV-256 | RTV-896 | RTV-899 | |
|---|---|---|---|---|---|---|
| Color | Translucent | Transparent | Transparent | White/red/trans. | Dark Grey | |
| Ration | by weight | 100:100 | 100:10:00 | 100:10:00 | 100:10:00 | 100:10:00 |
| Mix. Visc. | (*CpS)mPa.s | (7500)* | 50.000 | 50.000 | 25.000 | 45.000 |
| Pot life | min. | 20 | 90 | 90 | 60 | 60 |
| Gel time | min. | 15 | 50 | 45 | 30 | 30 |
| Demould time | Hours | 3 | 20 | 20 | 16-24 | 16-24 |
| Type of curing* | Addition | Addition | Addition | Addition | Addition | |
| Density Mixed | g/cm³ | 1,1 | 1,1 | 1,08 | 1,1 | 1,3 |
| Shore A | 33-35 | 40 | 34 | 28 | 50 | |
| Linear shrinkage | % | 0,1 | 0,1 | 0,1 | 0,1 | 0,1 |
| Tensile strength | Mpa | 5,7 | 6,5 | 5,5 | 7,5 | 5 |
| Elongation | % | 430 | 400 | 380 | 450 | 300 |
| Tear strength | N/mm | 18 | 18 | 14 | 20 | 8 |
| Shrinkage 40°C | % | |||||
| Shrinkage 60°C | % | |||||
| Expansion 40°C | % | |||||
| Temp. Resistans | °C | -70-+200 | -70-+280 | -50-+220 | -70-+220 | -70-+220 |
| Pack size | 20 kg A+ 20 kg B | 20 kg A+ 2 kg B | 20 kg of A + 2 kg B | 25 kg A + 2,5 kg B | 25 kg A+ 2,5 kg B | |
| Shelf life | 1 year | 1 year | 1 year | 1 year | 1 year | |
| Remarks/ Application | Rapid Prototyping | Rapid Prototyping | As RTV-250 but with extra release | High strength | Ceramics moulds |
Oils
Oils – PDF
Emulsion
Emulsion – PDF
Sealant (Fugemasse)
Sealant – PDF
Antifoams
Antifoams – PDF